9 Ways to Cut Costs in 2010
When it comes to cutting costs, there's something to be said for reviewing expenses, letting go of unnecessary staff and limiting discretionary e-xpenditures.
Read More
Removal of Ash After Burn-off
We currently utilize the burn-off method in order to clean the hangers. If I must invest in a high-pressure wash station, could this system replace the actual burn off?
Read More
Powder Palace
How a manufacturer of sporting goods turned its powder operation into the centerpiece of its plant to meet environmental guidelines and improve product quality
Read MorePowder over Liquid Paint
Can you tell me whether powder coating can be applied to painted components? I want to cover uncoated areas of pieces after electro-galvanneal is sprayed with zinc-rich paint.
Read More500-HR SALT-SPRAY REQUIREMENT
We have been experiencing some coating failures lately and we are trying to figure out how to find the root cause and what tests we can use to prevent them. We need to pass a 500-hr salt-spray requirement, and we cannot always meet the specification.
Read MoreUniform Coverage
We need suggestions on how to set up our racks and how to adjust our spray guns to get more uniform coverage on all four sides of the post.
Read MoreWhat is Causing Streaks?
We apply a medium-gloss gray powder at thickness of around 3–5 mils. Some of our panels have a large surface area and we sometimes get some streaks on the parts and areas that are darker than others. Any advice you can give us on the cause of the streaks and how to avoid them would be appreciated.
Read MoreDisposing of Waste Powder
Is there some way to use the over-sprayed powder instead of throwing it out? Are there any alternative ways to dispose of waste powder?
Read MoreRE-SPRAYING PARTS
I was under the impression that if you wanted to rework and re-spray over a powder coated part the following steps should take place for the best results. Please answer these questions for me.
Read MoreCHROMATE CONVERSION COATING
A potential client is sandblasting an aluminum substrate and applying 4–6 mils of a fairly standard white powder. The idea would be to save on powder material, as I would think 2–3 mils over chem film would be a great system. I am looking for information to support this suggestion. Can you also touch on what happens to the chem film when the powder is cured at nearly 400ºF?
Read More