Paint Test Panels
Can you help us locate a source for purchasing paint sample test panels?
Read MorePoor DOI Over Galvanized Steel
We would like to improve the Distinctness of Image (DOI) on our motorcycle fuel tanks and seek your advise for the same. The present surface texture is not very good, because the tank’s raw material is steel sheet galvanized on both sides. Please advise us what to do to solve the problem. Your reply in this regard will be highly appreciated.
Read MoreReplaced Liner Just Isn't The Same As The Old
The liner on our Osrotron 10-cu-ft bowl wore out and we decided to reline rather than purchase a new machine. When we got the bowl back with the new liner, we could not adjust the machine to the same good action we had before. Our supply vendor is not qualified to help with this. We don’t know where to turn for assistance since Osro is out of business.
Read MorePowder Adhesion to Anodized Parts
Are there any inherent problems with powder coating over black anodized aluminum parts? Is it better (or possible) to black anodize after powder coating?
Read MoreLoss of Adhesion and Corrosion Failure on CRS Frames
On some of the CRS frames (used to build industrial equipment) that I have used wherein we specify powder coating, I have noticed the paint peel off with heavy signs of rust underneath. Can you please help explain the reason for this and what it is you think the painter is doing wrong?
Read MoreHow to Fix Stripping Gold
We selectively strip gold from using a reel-to-reel process. Quite often, the gold that remains after the stripping process is a dark, brown-gold color. Do you have any suggestions for how to fix this problem?
Read MoreRecycling Spent Bulbs Revisited
We have a wastewater pretreatment system that consists of several sumps and holding tanks. For level control, we use mercury float switches. Periodically, these go bad and have to be replaced. Since spent fluorescent lamps contain mercury and can’t be thrown into our regular trash, what do we do about these switches?
Read MoreReactive Waste or Not Revisited
I would like more information on the organic sulfide precipitant described in the November 2006 column, “Reactive Waste or Not." Does it really work better than conventional neutralization/precipitation using acid/caustic and a flocculant?
Read MoreOverheated Nickel Sulfamate
We use a nickel sulfamate plating bath with a temperature range of 50–60°C to plate low stress micro-layers. Recently the temperature was allowed to reach 70°C. Did we ruin the plating bath because of this temperature upset? Can the plating bath be salvaged?
Read More